<?xml version="1.0" encoding="utf-8"?>
<rss version="2.0">
  <channel>
    <title>PP论坛 - 湿式复合</title>
    <link>https://www.slfhcy.com/forum.php?mod=forumdisplay&amp;fid=267</link>
    <description>Latest 20 threads of 湿式复合</description>
    <copyright>Copyright(C) PP论坛</copyright>
    <generator>Discuz! Board by Comsenz Inc.</generator>
    <lastBuildDate>Tue, 05 May 2026 16:30:05 +0000</lastBuildDate>
    <ttl>60</ttl>
    <image>
      <url>https://www.slfhcy.com/static/image/common/logo_88_31.gif</url>
      <title>PP论坛</title>
      <link>https://www.slfhcy.com/</link>
    </image>
    <item>
      <title>PVC复合</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=11515</link>
      <description><![CDATA[PVC复合针刺棉水胶复合的时候看起来还好，但放置一段时间上面有皱纹，请大神指教]]></description>
      <category>湿式复合</category>
      <author>迷茫的爱</author>
      <pubDate>Fri, 27 Nov 2015 08:06:20 +0000</pubDate>
    </item>
    <item>
      <title>请教个问题，无纺布用热熔胶复合需要电晕面吗？</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=10269</link>
      <description><![CDATA[问个问题，无纺布用热熔胶复合需要电晕面吗？

来自:Android客户端]]></description>
      <category>湿式复合</category>
      <author>包装印刷360</author>
      <pubDate>Sun, 14 Jun 2015 03:12:08 +0000</pubDate>
    </item>
    <item>
      <title>复合隧道问题探讨总结</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=9564</link>
      <description><![CDATA[对于复合产生隧道这个问题经常出现，我们一行人做了一些讨论，在这里我做一下总结，所谓隧道就是两张膜复合时不能完全的贴合形成隆起或凹陷的情况，也就是两张膜之间产生了蠕动，然而大多数人考虑的是胶水固化，温度，张力的问题，改变这些参数虽然能在一定程度上减轻问 ...]]></description>
      <category>湿式复合</category>
      <author>小狼</author>
      <pubDate>Fri, 12 Sep 2014 06:52:19 +0000</pubDate>
    </item>
    <item>
      <title>请教各位专家</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=9057</link>
      <description><![CDATA[复合的自动灌装卷材热封不住，一般都是什么原因造成的？请各位专家指点指点。]]></description>
      <category>湿式复合</category>
      <author>good-pack.com</author>
      <pubDate>Fri, 16 May 2014 03:27:50 +0000</pubDate>
    </item>
    <item>
      <title>请问pet/pe自动灌装卷材出现低总不热封，高温出现针孔化是什么问题？</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=9053</link>
      <description><![CDATA[12pet/88pe复合后灌装液体，现在反映说总出现针孔，经常出现漏袋。请问具体是什么原因，这种包装膜需要注意哪些方面？]]></description>
      <category>湿式复合</category>
      <author>good-pack.com</author>
      <pubDate>Thu, 15 May 2014 06:28:43 +0000</pubDate>
    </item>
    <item>
      <title>干复托层，烫口处不托层，请问是什么出现的问题？</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=9030</link>
      <description><![CDATA[pet12/pe88复合后，大面积托层，但烫口处没有问题，没有印刷。用的是150线的网线辊，请教各位是哪方面出现的问题？]]></description>
      <category>湿式复合</category>
      <author>good-pack.com</author>
      <pubDate>Wed, 07 May 2014 06:17:10 +0000</pubDate>
    </item>
    <item>
      <title>求推荐</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=7208</link>
      <description><![CDATA[求推荐湿法气味轻的胶水厂家 做PE透气复合膜]]></description>
      <category>湿式复合</category>
      <author>yw526</author>
      <pubDate>Sun, 14 Apr 2013 08:39:50 +0000</pubDate>
    </item>
    <item>
      <title>湿式复合主要用在哪些复合上面？</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=6356</link>
      <description><![CDATA[我见过的湿式复合，用在玻璃纤维布跟铝箔的复合上面，还有谁见过更多的，一起来分享探讨]]></description>
      <category>湿式复合</category>
      <author>Bruce</author>
      <pubDate>Wed, 09 Jan 2013 14:37:16 +0000</pubDate>
    </item>
    <item>
      <title>湿式复合文献贴-书签</title>
      <link>https://www.slfhcy.com/forum.php?mod=viewthread&amp;tid=6188</link>
      <description><![CDATA[此贴相当于书签作用，将发布到PP论坛里面的关于湿式复合的文献或者技术帖子，以标题和链接形式发布到该帖子下面，方便朋友们浏览和阅读。
如有朋友发布文献贴，请遵照以上方式跟帖，建立方便大家的书签。方便别人就是方便自己。
请该板块版主确保此贴顺畅，删除不合理跟 ...]]></description>
      <category>湿式复合</category>
      <author>Bruce</author>
      <pubDate>Sat, 29 Dec 2012 07:27:36 +0000</pubDate>
    </item>
  </channel>
</rss>